| Parameter | Details |
|---|---|
| Color | VITA 16 shades + BL1/BL2/BL3/BL4 |
| Type | All-In-One Block |
| Sintered Density | 6.0 g/cm³ |
| Bending Strength | 1350 MPa |
| Light Transmittance | 40% |
| Sintering Temperature | 1530°C |
Inlays, Onlays, Partial Crowns
Anterior Crown
Posterior Crown
Full Arch Crown Bridge
Screw-retained Full Contour Bridge
HTPC High Translucent Pre-colored Zirconia Block offers impressive strength (1350 MPa) and 40% translucency. It’s ideal for strong, long-lasting restorations with a natural, lifelike appearance. Perfect for copings, frameworks, and posterior crowns.
No more color matching—HTPC comes pre-colored, saving you time and hassle. Its fine-grain microstructure ensures smooth CAD/CAM milling, improving workflow efficiency and precision.
HTPC zirconia blocks are manufactured from premium raw materials through cold isostatic pressing, pre-sintering, and CNC precision machining to ensure high density and dimensional stability. Each block undergoes rigorous strength, color, and consistency testing prior to shipment, guaranteeing reliable quality and consistent performance.
From posterior restorations to full-arch crowns, HTPC delivers the strength and translucency you need. It’s a versatile material that doesn’t compromise on aesthetics or durability.
Available in 16 classical VITA shades and 4 bleach shades (BL1–BL4). For more natural results, Biomic Stain & Glaze can be applied.
| Opening System | Amann Girrbach | ZirkonZahn |
|---|---|---|
| 98×10mm | 89×71×10mm | 95×10mm |
| 98×12mm | 89×71×12mm | 95×12mm |
| 98×14mm | 89×71×14mm | 95×14mm |
| 98×16mm | 89×71×16mm | 95×16mm |
| 98×18mm | 89×71×18mm | 95×18mm |
| 98×20mm | 89×71×20mm | 95×20mm |
| 98×22mm | 89×71×22mm | 95×22mm |
| 98×25mm | 89×71×25mm | 95×25mm |
If you are interested in our products or have any questions, please contact us through the form below and add WhatsApp (+8613055185196)!
| Components | Content (%) |
|---|---|
| ZrO₂ + HfO₂ | ≥ 99.0 |
| Y₂O₃ | 4.0–10.0 |
| HfO₂ | ≤ 5.0 |
| Al₂O₃ | ≤ 0.1 |
| Other Oxides | ≤ 0.9 (Fe₂O₃, Er₂O₃, MnO) |
| Property | HT PLUS Value |
|---|---|
| Flexural Strength | 1350 MPa |
| Fracture Toughness | > 8.0 MPa·m¹ᐟ² |
| Translucency | 40% |
| Sintered Density | 6.0 g/cm³ |
| Chemical Solubility | < 100 μg/cm² |
| Shrinkage Factor | 1.220–1.260 (±0.002) |
| Radioactivity | < 1.0 Bq·g⁻¹ (U-238) |
| Thermal Expansion Coefficient | 10.4 ± 0.5 × 10⁻⁶ K⁻¹ |
| HTPC Sintering Curve | ||||
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time (Min) | Rate (℃/Min) |
| Step 1 | 20 | 300 | 70 | 4 |
| Step 2 | 300 | 1000 | 175 | 4 |
| Step 3 | 1000 | 1530 | 177 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 146 | -5 |
| Step 6 | 800 | natural cooling 20 | / | / |